Magnetite nanoparticles have been prepared by electrooxidation of iron in water. Surface modifications

have been conducted by coating the nanoparticles with silica by a one-step synthesis in dilute sodium

silicate solution. The mean size of particles was approximately 10–30 nm for the uncoated particles

and 9–12 nm for the coated particles. The results obtained from thermal gravimetric/differential thermal

analysis (TG/DTA) revealed that the silica layer formed by the electrochemical method was stable and

could serve as a protective layer. Annealing the nanoparticles at 550 C for 30 min converts magnetite

into maghemite for the silica-coated particles, and it further converts the uncoated particles into hematite.

The conversions cause the saturation magnetization to decrease for all samples.